Reliability of aluminized integrated circuits
// Electronics and Machinery. – 2017. – ¹ 3.
– P. 1 - 6.
Read the article
Review: Aluminium with its alloys is the basic material of integrated circuits metallization. Use of VLSIC toughens the requirements to the parameters of metallization, which determine its reliability, such as surface resistance, step coating quality, number and sizes of tension-caused voids, and electromigration tolerance. Poor quality of metallization is one of the most dangerous defects in semiconductor technology of integrated circuits. Electromigration can cause failure when passing high-density current through metallization. The materials have been tested in order to estimate the intensity of metal resistance variation caused by electromigration. Based on the results of these tests, the authors conclude that geometrical factors play a dominant role in the mechanism of erosion of integrated circuits metallization caused by electromigration. With regard to the tests, the authors formulate recommendations about the transition from the sputtering technique to evaporation deposition.
Keywords: semiconductor, electronics, technology, electromigration, aluminum, circuit, metallization, connection, silicon, reliability
Mustafaev G.A., Uyanaeva M.M., Panchenko V.A. Silitsidy tugoplavkikh materialov v tekhnologii SBIS // Materialy Mezhdunarodnoy nauchno-tekhnicheskoy konferentsii «Mikro- i nanotekhnologii v elektronike», Nal'chik, 2009, s.212-216.
Chou Y.-H., Sung Y., Bai C.-Y., Ger M.-D. Effects of molybdate concentration on the characteristics of Ni–Mo–P diffusion barriers grown by nonisothermal electroless deposition // J. Electrochem. Soc. 2008, v.155, ¹9, p.D551 - D557.
Mustafaev G.A., Uyanaeva M.M., Mustafaev A.G. Vzaimodeystvie sloev v sisteme Al-NiSi pri nalichii podsloya vol'frama // Materialy IV Mezhdunarodnoy nauchno-tekhnicheskoy konferentsii «Mikro- i nanotekhnologii v elektronike», Nal'chik, 2011, s.184-185.
Margolin V.I., Zharbeev V.A., Tupik V.A. Fizicheskie osnovy mikroelektroniki. M.: Akademiya, 2008 – 400 s.
Mustafaev G.A., Mustafaev A.G., Mustafaev A.G., Cherkesova N.V. Sposob izgotovleniya kontaktno-bar'ernoy metallizatsii // Patent RF 2550586. Byul. 13, 2015 g.
Poller T., Lutz J., Böttge B., Knoll H. Analysis of